Structurally viscose clear lacquer slurry, method for the production and use thereof

ABSTRACT

A pseudoplastic clearcoat slurry comprising solid and/or highly viscous particles which are dimensionally stable under storage and application conditions and at least one wetting agent selected from the group consisting of alkoxylated fatty alcohols having from 16 to 18 carbon atoms in the alkyl radical and containing on average per molecule at least 20 oxaalkanediyl groups; process for preparing it, and its use.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a National Phase Application of Patent Application PCT/EP02/08170 filed on 23 Jul. 2002, which claims priority to DE 101 35 998.5, filed on 24 Jul. 2001.

The present invention relates to a novel pseudoplastic clearcoat slurry. The present invention also relates to a novel process for preparing pseudoplastic clearcoat slurries. The present invention additionally relates to the use of the novel pseudoplastic clearcoat slurry for automotive OEM finishing, automotive refinish, the interior and exterior painting of buildings, the coating of doors, windows and furniture, and industrial coating, including coil coating, container coating, the coating of small parts, the impregnation and/or coating of electrical components, and the coating of white goods. The present invention relates not least to the use of the novel clearcoat slurries as adhesives and sealing compounds for producing adhesive films and seals, especially in the aforementioned fields.

The German patent application DE 196 17 086 A1 discloses a powder clearcoat slurry preparable by means of a secondary dispersion process in which the dispersing equipment comprises pressure release homogenizing nozzles. For stabilizing in addition to the ionic stabilization, it is necessary to employ external emulsifiers or wetting agents as well, but these are not specified in any greater detail. Moreover, these known clearcoat slurries always include certain amounts of organic cosolvents or leveling agents, which cannot be removed as they are essential for the leveling properties of the initially dried film. Prior to the application of the clearcoat slurries, they are adjusted to the application viscosity using thickeners; a complex viscosity behavior, however, is not described.

A comparable clearcoat slurry is known from the European patent application EP 0 899 282 A2. The known clearcoat slurry may be prepared by a direct dispersion process or by the phase inversion process. By the phase inversion process is meant the secondary dispersion process set out below. It is important that preparation is carried out using a dispersing apparatus having a volume-related dispersing output of from 1×10 to 9.8×10 000 W/cm³. For their stabilization, the known clearcoat slurries require external emulsifiers or wetting agents of which no further details are given; a complex viscosity behavior is not described.

In this situation, the pseudoplastic clearcoat slurry known from the German patent DE 198 41 842 C2 provided substantial advances.

The known pseudoplastic clearcoat slurry is free from organic solvents and external emulsifiers and comprises solid spherical particles with an average size of from 0.8 to 20 μm and a maximum size of 30 μm, the clearcoat slurry having an ion-forming group content of from 0.05 to 1 meq/g, a neutralizing agent content of from 0.05 to 1 meq/g, and a viscosity of

-   -   (i) from 50 to 1 000 mPas at a shear rate of 1 000 s⁻¹,     -   (ii) from 150 to 8 000 mPas at a shear rate of 10 s⁻¹, and     -   (iii) from 180 to 12 000 mPas at a shear rate of 1 s⁻¹.

The known pseudoplastic clearcoat slurry is prepared by

-   -   1) emulsifying an organic solution comprising binder and         crosslinking agent in water, to give an emulsion of the         oil-in-water type,     -   2) removing the organic solvent or the organic solvents, and     -   3) replacing by water some or all of the solvent removed, to         give a clearcoat slurry comprising solid spherical particles,     -   where     -   4) additionally, at least one ionic, especially anionic,         thickener and at least one nonionic associative thickener are         added to the clearcoat slurry.

Here and below, the process in accordance with steps (1) to (3) is referred to as the secondary dispersion process.

This clearcoat slurry is preparable with a small number of processing steps; on the basis of its typical powder slurry properties, with residual solvent contents of <1%, and its particle sizes, it exhibits advantageous application properties. Even without the assistance of organic solvents, there is generally no popping at the required film thickness of approximately 40 to 50 μm. Moreover, the particles of the slurry, owing to mixing of their constituents in solution, are very homogeneous. The resulting clearcoats are bright, chemical-resistant, and flow out very well, without popping marks or cracking.

The clearcoat slurries are highly suitable for the production of clearcoats for high-quality multicoat color and/or effect paint systems, such as are used to coat automobiles, for example. In the production of these multicoat color and/or effect paint systems, the clearcoat slurries may be used by the wet-on-wet technique in combination with any of a very wide variety of aqueous basecoat materials, without the occurrence of deleterious effects such as mudcracking.

In the German patent application DE 100 01 442.9, unpublished at the priority date of the present specification, the clearcoat slurry of the German patent DE 198 41 842 C2 is subsequently subjected to wet grinding.

In the German patent application DE 100 55 464.4, unpublished at the priority date of the present specification, a pseudoplastic clearcoat slurry free from organic solvents and external emulsifiers is described which comprises solid and/or highly viscous particles which are dimensionally stable under storage and application conditions,

-   -   1. said particles         -   1.1 having an average particle size of from 1.0 to 20 μm, at             least 99% of the particles having a size ≦30 μm, and         -   1.2 containing as binder at least one polyol with an OH             number >110 mg KOH/g, containing potentially ionic groups,     -   and     -   2. said clearcoat slurry         -   2.1 containing from 0.01 to 1 meq of potentially ionic             groups per g of solids,         -   2.2 containing, at a degree of neutralization of not more             than 50%, an amount of ionic groups produced by             neutralization of the potentially ionic groups of from 0.005             to 0.1 meq/g of solids, and         -   2.3 having a viscosity of (i) from 50 to 1 000 mPas at a             shear rate of 1 000 s⁻¹, (ii) from 150 to 8 000 mPas at a             shear rate of 10 s⁻¹, and (iii) from 180 to 12 000 mPas at a             shear rate of 1 s⁻¹.

The pseudoplastic clearcoat slurries may again be prepared by the secondary dispersion process.

The German patent application DE 100 27 290.8, unpublished at the priority date of the present specification, describes clearcoat slurries which may be prepared, inter alia, by the secondary dispersion process. The essential constituent of the clearcoat slurries is at least one adduct of ethylene oxide and/or propylene oxide with at least one glycol, especially ethylene glycol, 1,3- and/or 1,2-propylene glycol or 1,2-, 1,3- and/or 1,4-butylene glycol. Examples of highly suitable adducts are polyethylene glycols, polypropylene glycols, block copolymers of ethylene oxide and propylene oxide (Pluronics®) or polytetramethylene glycols (polytetrahydrofurans) (cf. Römpp Lexikon Lacke und Druckfarben, Georg Thieme Verlag, 1998, page 457, “Polyalkylene glycols”), of which the adducts of propylene oxide with 1,3- and/or 1,2-propylene glycol, i.e. the polypropylene glycols, are particularly advantageous and are therefore used with particular preference in accordance with the invention. Particularly suitable polypropylene glycols have a number-average molecular weight of from 350 to 1 000, preferably from 400 to 950, with particular preference from 450 to 900, with very particular preference from 500 to 850, and in particular from 550 to 800 daltons. The polypropylene glycols are commercial products and are sold, for example, by BASF Aktiengesellschaft under the brand name Pluriol® 400, 600 and 900, the numerical suffixes indicating the molecular weight or its order of magnitude. The amount of the adducts in the clearcoat slurries is preferably from 0.01 to 2.0% by weight, based in each case on the solids of a given clearcoat slurry. The adducts are added to the clearcoat slurries prior to wet grinding.

Since the clearcoat slurries have to be filtered prior to their application, it is important that they possess good filterability. In the plants of the users, especially on the lines of the automobile manufacturers, they are conveyed through gear pumps. This exposure to load, however, may significantly impair their filterability. The impaired filterability of the load-exposed clearcoat slurries results in clearcoats having impaired optical properties (appearance). Addition of external emulsifiers or wetting agents frequently improves the filterability but impairs the gear-pump conveyability and the pseudo-plasticity of the clearcoat slurries, and also the chemical resistance of the clearcoats produced from them.

It is an object of the present invention to provide a novel pseudoplastic clearcoat slurry which no longer has the disadvantages of the prior art but which instead combines good filterability with good gear-pump conveyability. The novel pseudoplastic clearcoat slurry ought to provide clearcoats which in terms of their optical properties (appearance) and chemical resistance are at least equal to the clearcoats produced from the known clearcoat slurries.

The invention accordingly provides the novel pseudo-plastic clearcoat slurry comprising solid and/or highly viscous particles which are dimensionally stable under storage and application conditions and at least one wetting agent selected from the group consisting of alkoxylated fatty alcohols having from 16 to 18 carbon atoms in the alkyl radical and containing on average per molecule at least 20 oxaalkanediyl groups.

In the text below, the novel pseudoplastic clearcoat slurry is referred to as the “slurry of the invention”.

Further subject matter of the invention will emerge from the description.

In the light of the prior art it was surprising for the skilled worker, and, unforeseeable, that the object on which the present invention is based could be achieved by adding small amounts of specially selected wetting agents to conventional clearcoat slurries. This was all the more surprising since the prior art bears no indications of any correlation between the wetting agents for use in accordance with the invention, on the one hand, and the filterability and gear-pump conveyability of clearcoat slurries, on the other.

The slurries of the invention may be of various compositions. For example,

-   -   the clearcoat slurries known from the German patent applications         DE 195 40 977 A1 or DE 19832 2 06 A1, prepared by means of         grinding and dispersing processes and curable thermally or with         actinic radiation,     -   the clearcoat slurries known from the German patent application         DE 199 59 923 A1, prepared by means of primary dispersion         processes and curable thermally or both thermally and with         actinic radiation,     -   the clearcoat slurries known from the international patent         applications WO 97/45476, WO 98/45356 or WO 00/17256 or from the         American patent U.S. Pat. No. 4,056,653 A, or described in the         German patent applications DE 100 06 673.9 or DE 100 18 581.9,         both unpublished at the priority date of the present         specification, prepared by means of melt emulsification         processes and curable thermally or both thermally and with         actinic radiation, or     -   the clearcoat slurries known from the German patent applications         DE 198 41 842 A1, DE 196 17 086 A1 or DE 199 08 018 A1 or from         the European patent application EP 0 899 282 A1, or described in         the German patent application DE 100 55 464.4, unpublished at         the priority date of the present specification, prepared by         means of secondary dispersion processes and curable thermally or         both thermally and with actinic radiation         are a typical basis for the slurries of the invention.

Of these, the clearcoat slurries known from the German patent applications DE 198 41 842 A1 or DE 199 08 018 A1 or described in the German patent application DE 100 55 464.4, unpublished at the priority date of the present specification, prepared by means of secondary dispersion processes and curable thermally or both thermally and with actinic radiation, which are free or substantially free from organic solvents, are of advantage and are therefore used with preference in accordance with the invention.

Very particular preference is given to the clearcoat slurries prepared by the secondary dispersion process and comprising the specific methacrylate copolymers described below as binders in the dimensionally stable particles.

The slurry of the invention comprises as a constituent essential to the invention at least one, especially one, wetting agent selected from the group consisting of alkoxylated fatty alcohols having from 16 to 18 carbon atoms in the alkyl radical and containing on average per molecule at least 20, preferably at least 25, more preferably at least 30, with particular preference at least 35, with very particular preference at least 40, and in particular at least 45, oxaalkane-diyl groups.

Suitable oxaalkanediyl groups are 1-oxapropane-1,3-diyl, 1-oxabutane-1,4-diyl, 1-oxabutane-1,3-diyl, 1-oxapentane-1,5-diyl, and 1-oxapentane-1,3-diyl, preferably 1-oxapropane-1,3-diyl and 1-oxabutane-1,3-diyl, especially 1-oxapropane-1,3-diyl (ethylene oxide group).

The wetting agent may contain at least two kinds of these oxaalkanediyl groups. The oxaalkanediyl chains may be random, alternating or blocklike in structure. Preferably, the wetting agent contains only one kind of oxaalkanediyl groups, in particular the ethylene oxide groups.

The wetting agents used with preference in accordance with the invention, from the group of the fatty alcohols having from 16 to 18 carbon atoms in the alkyl radical and containing at least 20 ethylene oxide groups in the molecule, are commercially customary compounds and are sold, for example, by BASF Aktiengesellschaft under the brand name Lutensol® AT 25 (25 ethylene oxide groups in the molecule) and AT 50 (50 ethylene oxide groups in the molecule).

The wetting agents for use in accordance with the invention are used preferably in an amount of from 0.01 to 2.5% by weight, more preferably from 0.05 to 2.4% by weight, with particular preference from 0.1 to 2.2% by weight, with very particular preference from 0.15 to 2% by weight, and in particular from 0.2 to 1.8% by weight, based in each case on a given clearcoat slurry.

The slurry of the invention comprises dimensionally stable particles. In the context of the present invention, “dimensionally stable” means that, under the customary known conditions of storage and application of clearcoat slurries, the particles undergo little if any agglomeration and/or breakdown into smaller particles, but instead substantially retain their original form even under the influence of shear forces. The particles may be highly viscous and/or solid. Preferably, the dimensionally stable particles are solid.

For the slurry of the invention it is advantageous if the average size of the particles is from 1 to 20 μm and with particular preference from 3 to 15 μm. By average particle size is meant the 50% median value as determined by the laser diffraction method, i.e., 50% of the particles have a diameter ≦the median value and 50% of the particles have a diameter ≧the median value. Preferably, at least 99% of the particles have a size <30 μm.

Slurries having average particle sizes of this kind and a solvent content of <1% exhibit better application properties and, at the applied film thicknesses of >30 μm as presently practiced in the automobile industry for the finishing of automobiles, exhibit much less of a tendency toward popping marks and mudcracking than conventional clearcoat slurries.

The upper limit on particle size is reached when the size of the particles means that they are no longer able to flow out fully on baking, and thus film leveling is adversely affected. In cases where requirements regarding the appearance are not very stringent, however, the limit may also be higher. 30 μm is considered a sensible upper limit, since above this particle size the spray nozzles and the rinsing ducts of the highly sensitive application apparatus are likely to become blocked.

The slurry of the invention is, preferably, substantially or entirely free from organic solvents. In the context of the present invention this means that it has a residual volatile solvent content of <3% by weight, preferably <2% by weight, and with particular preference <1% by weight.

The slurry of the invention preferably contains from 0.05 to 1, more preferably from 0.05 to 0.9, more preferably still from 0.05 to 0.8, with particular preference from 0.05 to 0.7, and in particular from 0.05 to 0.6 meq of potentially ionic groups per g of solids. The amount of neutralizing agents is preferably chosen such that the degree of neutralization is 100%, preferably below 80%, with particular preference below 60%, and in particular below 50%.

The chemical nature of the binder is generally not restricting in this respect, provided it contains ion-forming groups which can be converted into salt groups by neutralization and which, as a result, are able to take over the function of ionic stabilization of the particles in water.

Suitable anion-forming groups include acid groups such as carboxylic acid, sulfonic acid or phosphonic acid groups, especially carboxylic acid groups. Accordingly, bases, such as alkali metal hydroxides, ammonia or amines, are used as neutralizing agents. Alkali metal hydroxides can be used only to a limited extent, since the alkali metal ions are not volatile on baking and, owing to their incompatibility with organic substances, may cause the film to become cloudy and may lead to loss of gloss. Therefore, ammonia or amines are preferred. In the case of amines, tertiary amines are preferred. By way of example, mention may be made of N,N-dimethylethanolamine or aminomethylpropanolamine (AMP).

Suitable cation-forming groups include primary, secondary and tertiary amines. Accordingly, neutralizing agents used are, in particular, low molecular mass organic acids such as formic acid, acetic acid, dimethylolpropionic acid or lactic acid.

For the preferred use of the slurry of the invention in automobile finishing as an unpigmented clearcoat material, preference is given to polymers or oligomers containing acid groups as ion-forming groups, since these so-called anionic binders generally exhibit better resistance to yellowing than the class of the cationic binders.

However, cationic binders containing groups which can be converted into cations, such as amino groups, are likewise suitable for use in principle, provided the field of use tolerates their typical secondary properties such as their tendency toward yellowing.

Examples of suitable binders are random, alternating and/or block, linear and/or branched and/or comb, addition (co)polymers of ethylenically unsaturated monomers, or polyaddition resins and/or poly-condensation resins. For further details of these terms, refer to Römpp Lexikon Lacke und Druckfarben, Georg Thieme Verlag, Stuttgart, N.Y., 1998, page 457, “polyaddition” and “polyaddition resins (poly-adducts)”, and also pages 463 and 464, “poly-condensates”, “polycondensation” and “polycondensation resins”, and also pages 73 and 74, “binders”.

Examples of suitable addition (co)polymers are (meth)acrylate (co)polymers or partially saponified polyvinyl esters, especially (meth)acrylate copolymers.

Examples of suitable polyaddition resins and/or polycondensation resins are polyesters, alkyds, polyurethanes, polylactones, polycarbonates, poly-ethers, epoxy resins, epoxy resin-amine adducts, polyureas, polyamides, polyimides, polyester-polyurethanes, polyether-polyurethanes or polyester-polyether-polyurethanes.

These oligomers and polymers are known to the skilled worker, and many suitable compounds are available on the market.

In accordance with the invention the (meth)acrylate copolymers, the polyesters, the alkyd resins, the polyurethanes and/or the acrylated polyurethanes are of advantage and are therefore used with preference.

Highly suitable (meth)acrylate copolymers and processes for preparing them are described, for example, in the German patent application DE 199 08 018 A1, page 9, line 44, to page 10, line 53, in the European patent application EP 0 767 185 A1, in the German patents DE 22 14 650 B1 and DE 27 49 576 B1, and in the American patents U.S. Pat. Nos. 4,091,048 A, 3,781,379 A, 5,480,493 A, 5,475,073 A, and 5,534,598 A, or in the standard work by Houben-Weyl, Methoden der organischen Chemie, 4th edition, volume 14/1, pages 24 to 255, 1961. Suitable reactors for the copolymerization include the customary and known stirred tanks, stirred tank cascades, tube reactors, loop reactors or Taylor reactors, as are described, for example, in the patent applications DE 1 071 241 B1, EP 0 498 583 A1 or DE 198 28 742 A1 or in the article by K. Kataoka in Chemical Engineering Science, volume 50, No. 9, 1995, pages 1409 to 1416.

Highly suitable polyesters and alkyd resins, and their preparation, are described, for example, in the standard work Ullmans Encyklopädie der technischen Chemie, 3rd edition, volume 14, Urban & Schwarzenberg, Munich, Berlin, 1963, pages 80 to 89 and pages 99 to 105, and also in the following books: “Résines Alkydes-Polyesters” by J. Bourry, Dunod, Paris, 1952, “Alkyd Resins” by C. R. Martens, Reinhold Publishing Corporation, New York, 1961, and, “Alkyd Resin Technology” by T. C. Patton, Interscience Publishers, 1962.

Highly suitable polyurethanes and/or acrylated polyurethanes and their preparation are described, for example, in the patents EP 0 708 788 A1, DE 44 01 544 A1 or DE 195 34 361 A1.

Very particular advantages result for the slurries of the invention if their dimensionally stable particles comprise as binder(s) at least one methacrylate copolymer which contains in copolymerized form, based on a given methacrylate copolymer, at least 90% by weight, preferably at least 95% by weight, and in particular at least 99% by weight of methacrylate comonomers, including methacrylate comonomers containing potentially ionic groups.

Preferably, the (meth)acrylate comonomers containing potentially ionic groups comprise acrylic acid, beta-carboxyethyl acrylate and/or methacrylic acid, especially methacrylic acid. The (meth)acrylate comonomers containing potentially ionic groups are preferably copolymerized into the methacrylate copolymers in an amount such that the above-described amount of potentially ionic groups in the particles can be set without problems. They are copolymerized into the methacrylate copolymers preferably in an amount of from 0.1 to 3%, more preferably from 0.2 to 2.8%, with particular preference from 0.3 to 2.6%, with very particular preference from 0.4 to 2.4%, and in particular from 0.5 to 2.2% by weight, based in each case on a given methacrylate copolymer.

The methacrylate copolymers preferably have a glass transition temperature, Tg, of not more than 50° C.; at the same time the glass transition temperature Tg should not go below preferably 0° C., more preferably 10° C., and in particular 20° C.

The glass transition temperature, Tg, of the methacrylate copolymers is preferably set by way of at least one methacrylate comonomer which is free from reactive functional groups and from potentially ionic groups. More preferably, the glass transition temperature, Tg, is set by way of at least two, in particular two, methacrylate comonomers which are free from reactive functional groups and from potentially ionic groups. Preferably, the glass transition temperatures, Tg, of the respective homopolymers of the methacrylate comonomers that are free from reactive functional groups and from potentially ionic groups differ from one another by not more than 40° C.

Examples of suitable methacrylate comonomers free from reactive functional groups and from potentially ionic groups are methyl, ethyl, n-propyl, n-butyl, i-butyl, tert-butyl, n-pentyl, isoamyl, cyclopentyl, n-hexyl and cyclohexyl methacrylate. Of these, i-butyl methacrylate (glass transition temperature, Tg, of the homopolymer: 53° C.) and n-butyl methacrylate (glass transition temperature, Tg, of the homopolymer: 20° C.) are of advantage and are therefore used with particular preference.

The amount of the copolymerized methacrylate comonomers, free from reactive functional groups and from potentially ionic groups, that is copolymerized into the methacrylate copolymers for use in accordance with the invention may vary widely. It is essential that the amount is chosen such that the resulting methacrylate copolymers have the glass transition temperature, Tg, described above. The amount is preferably at least 50%, more preferably at least 55%, with particular preference at least 60%, with very particular preference at least 65%, and in particular at least 70% by weight, based in each case on a given methacrylate copolymer.

The weight ratio of the methacrylate comonomers used with particular preference, n-butyl methacrylate and i-butyl methacrylate, may vary widely. The n:i weight ratio is preferably from 10:1 to 1:6, more preferably from 8:1 to 1:4, with particular preference from 6:1 to 1:2, with very particular preference from 5:1 to 1:1.5, and in particular from 4:1 to 1:1.

Where the slurries of the invention are physically curable slurries, the methacrylate copolymers contain reactive functional groups, if at all, only in a number which is insubstantial as far as crosslinking is concerned.

Where the slurries of the invention are thermally self-crosslinking, the methacrylate copolymers contain the complementary reactive functional groups for thermal crosslinking, described below, and/or reactive functional groups which are able to crosslink “with themselves”, i.e., with groups of their own kind.

Where the slurries of the invention are curable with actinic radiation, the methacrylate copolymers may contain reactive functional groups having at least one bond which can be activated with actinic radiation. These reactive functional groups are mandatorily present in the methacrylate copolymers of the slurries of the invention that are curable with actinic radiation if the slurries contain no other radiation-curable constituents.

Where the slurries of the invention are dual-cure slurries, the methacrylate copolymers contain reactive functional groups for thermal crosslinking and/or reactive functional groups containing at least one bond which can be activated with actinic radiation. The reactive functional groups containing at least one bond which can be activated with actinic radiation are mandatorily present in the methacrylate copolymers of the dual-cure slurries of the invention if the dual-cure slurries contain no other radiation-curable constituents.

Examples of suitable complementary reactive functional groups for use in accordance with the invention are placed together in the following overview. In the overview, the variable R stands for an acyclic or cyclic aliphatic radical, an aromatic radical and/or an aromatic-aliphatic (araliphatic) radical; the variables R′ and R″ stand for identical or different aliphatic radicals or are linked with one another to form an aliphatic or heteroaliphatic ring.

Overview: Examples of complementary reactive functional groups Binder and crosslinking agent or Crosslinking agent and binder —SH —C(O)—OH —NH₂ —C(O)—O—C(O)— —OH —NCO —O—(CO)—NH—(CO)—NH₂ —NH—C(O)—OR —O—(CO)—NH₂ —CH₂—OH >NH —CH₂—O—R —NH—CH₂—O—R —NH—CH₂—OH —N(—CH₂—O—R)₂ —NH—C(O)—CH(—C(O)OR)₂ —NH—C(O)—CH(—C(O)OR)(—C(O)—R) —NH—C(O)—NR′R″ >Si(OR)₂

—C(O)—OH

—C(O)—N(CH₂—CH₂—OH)₂

The selection of the respective complementary reactive functional groups is guided on the one hand by the consideration that they should not enter into any unwanted reactions during the preparation of the binders and during the preparation, storage, application, and melting of the slurries of the invention, and in particular should not form any polyelectrolyte complexes or undergo premature cross-linking, and/or must not disrupt or inhibit curing with actinic radiation, and secondly by the temperature range within which crosslinking is to take place.

For the slurries of the invention it is preferred to employ crosslinking temperatures of from 60 to 180° C. Use is therefore made preferably of binders containing thio, hydroxyl, N-methylolamino, N-alkoxymethylamino, imino, carbamate, and/or allophanate groups, preferably hydroxyl groups, on the one hand and, preferably, crosslinking agents containing anhydride, epoxy, blocked and unblocked, especially blocked, isocyanate, urethane, methylol, methylol ether, siloxane, carbonate, amino, hydroxyl and/or beta-hydroxyalkylamide groups, preferably blocked isocyanate, carbamate and/or N-alkoxymethylamino groups, on the other.

In the case of self-crosslinking slurries of the invention, the binders contain, in particular, methylol, methylol ether and/or N-alkoxymethylamino groups.

Complementary reactive functional groups which are especially suitable for use in the thermally externally crosslinking slurries of the invention and the dual-cure slurries of the invention are hydroxyl groups on the one hand and blocked isocyanate groups on the other.

The functionality of the binders in respect of the reactive functional groups described above may vary very widely and is guided in particular by the desired crosslinking density and/or by the functionality of the crosslinking agents that are employed in each case. In the case of hydroxyl-containing binders, for example, the OH number is preferably from 20 to 300, more preferably from 40 to 250, with particular preference from 60 to 200, with very particular preference from 80 to 190, and in particular from 90 to 180 mg KOH/g.

The above-described complementary reactive functional groups may be incorporated into the binders in accordance with the customary and known methods of polymer chemistry. This can be done, for example, through the incorporation of methacrylate comonomers which carry the corresponding reactive functional groups, and/or with the aid of polymer-analogous reactions.

Examples of suitable methacrylate comonomers containing reactive functional groups are methacrylate comonomers which carry at least one hydroxyl, amino, alkoxymethyl-amino, carbamate, allophanate or imino group per molecule, such as

-   -   hydroxyalkyl esters of methacrylic acid, which are derived from         an alkylene glycol which is esterified with the acid, or which         are obtainable by reaction of the methacrylic acid with an         alkylene oxide such as ethylene oxide or propylene oxide,         especially hydroxyalkyl esters of methacrylic acid in which the         hydroxyalkyl group contains up to 20 carbon atoms, such as         2-hydroxy-ethyl, 2-hydroxypropyl, 3-hydroxypropyl,         3-hydroxybutyl or 4-hydroxybutyl methacrylate; or         hydroxycycloalkyl esters such as         1,4-bis(hydroxy-methyl)cyclohexane,         octahydro-4,7-methano-1H-indenedimethanol or methylpropanediol         monometh-acrylate; or reaction products of cyclic esters, such         as epsilon-caprolactone, and these hydroxy-alkyl methacrylates;     -   reaction products of methacrylic acid of the glycidyl ester of         an alpha-branched monocarboxylic acid having from 5 to 18 carbon         atoms per molecule, particularly a Versatic® acid, or instead of         the reaction product an equivalent amount of methacrylic acid,         which is then reacted, during or after the polymerization         reaction, with the glycidyl ester of an alpha-branched         monocarboxylic acid having from 5 to 18 carbon atoms per         molecule, particularly a Versatic® acid;     -   aminoethyl methacrylate or N-methylaminoethyl methacrylate,         which may also be used to introduce potentially ionic groups;     -   N,N-di(methoxymethyl)aminoethyl methacrylate or         N,N-di(butoxymethyl)aminopropyl methacrylate;     -   methacrylamides such as methacrylamide, N-methyl-, N-methylol-,         N,N-dimethylol-, N-methoxymethyl-, N,N-di(methoxymethyl)-,         N-ethoxymethyl- and/or N,N-di(ethoxyethyl)-methacrylamide;     -   methacryloyloxyethyl, -propyl or -butyl carbamate or         allophanate; further examples of suitable methacrylate         comonomers containing carbamate groups are described in the         patents U.S. Pat. Nos. 3,479,328 A, 3,674,838 A, 4,126,747 A,         4,279,833 A or 4,340,497 A.

In minor amounts, the reactive functional groups for thermal crosslinking may be introduced by way of other olefinically unsaturated monomers, such as the corresponding acrylates, allylamine, allyl alcohol or polyols, such as trimethylolpropane monoallyl or diallyl ether or pentaerythritol monoallyl, diallyl or triallyl ether.

The binders of the dual-cure slurries may contain on average per molecule at least one, preferably at least two, group(s) containing at least one bond which can be activated with actinic radiation.

In the context of the present invention, a bond which can be activated with actinic radiation means a bond which, on exposure to actinic radiation, becomes reactive and, together with other activated bonds of its kind, enters into polymerization reactions and/or crosslinking reactions which proceed in accordance with free-radical and/or ionic mechanisms. Examples of suitable bonds are carbon-hydrogen single bonds or carbon-carbon, carbon-oxygen, carbon-nitrogen, carbon-phosphorus or carbon-silicon single bonds or double bonds. Of these, the carbon-carbon double bonds are particularly advantageous and are therefore used with very particular preference in accordance with the invention. For the sake of brevity, they are referred to below as “double bonds”.

Accordingly, the group that is preferred in accordance with the invention contains one double bond or two, three or four double bonds. Where more than one double bond is used, the double bonds may be conjugated. In accordance with the invention, however, it is of advantage if the double bonds are present in isolation, in particular each terminally, within the group in question. It is of particular advantage in accordance with the invention to use two double bonds, especially one double bond.

The dual-cure binder contains on average at least one of the above-described groups which can be activated with actinic radiation. This means that the functionality of the binder in this respect is integral, i.e., for example, is two, three, four, five or more, or is nonintegral, i.e., for example, is from 2.1 to 10.5 or more. The decision as to which functionality is chosen is guided by the requirements which are imposed on the respective dual-cure slurries.

Where on average per molecule more than one group which can be activated with actinic radiation is used, the groups are structurally different from one another or of the same structure.

Where they are structurally different from one another, this means in the context of the present invention that two, three, four or more, but especially two, groups which can be activated with actinic radiation are used which derive from two, three, four or more, but especially two, monomer classes.

Examples of suitable groups are (meth)acrylate, ethacrylate, crotonate, cinnamate, vinyl ether, vinyl ester, dicyclopentadienyl, norbornenyl, isoprenyl, isopropenyl, allyl or butenyl groups; dicyclo-pentadienyl ether, norbornenyl ether, isoprenyl ether, isopropenyl ether, allyl ether or butenyl ether groups; dicyclopentadienyl ester, norbornenyl ester, isoprenyl ester, isopropenyl ester, allyl ester or butenyl ester groups, but especially acrylate groups.

The groups are attached to the respective parent structures of the binders preferably by way of urethane, urea, allophanate, ester, ether and/or amide groups, but in particular by way of ester groups. This is normally done by means of customary and known continuous polymer-analogous reactions such as, for instance, the reaction of pendant glycidyl groups with olefinically unsaturated comonomers containing an acid group, of pendant hydroxyl groups with the halides of these comonomers, of hydroxyl groups with isocyanates containing double bonds, such as vinyl isocyanate, methacryloyl isocyanate and/or 1-(1-isocyanato-1-methylethyl)-3-(1-methylethenyl)benzene (TMI® from CYTEC), or of pendant isocyanate groups with the hydroxyl-containing comonomers described above.

In the particles it is, however, also possible to employ mixtures of binders that are curable by means of heat alone and of binders that are curable by means of actinic radiation alone.

Processes for preparing the methacrylate copolymers used with preference are known from the patent applications, patents and literature references cited above. With particular preference, the methacrylate copolymers are prepared under pressure.

The amount of the binders described above in the dimensionally stable particles may vary widely. In the case of the thermally externally crosslinking or of the thermally externally crosslinking and actinic-radiation-curable slurries of the invention said amount is preferably from 5 to 80%, more preferably from 6 to 75%, with particular preference from 7 to 70%, with very particular preference from 8 to 65% and in particular from 9 to 60% by weight, based in each case on the solids of the slurries of the invention. In the case of the slurries of the invention that are curable physically and those that are curable with actinic radiation, but especially those that are curable physically, the amount may be up to 100% by weight.

The dimensionally stable particles of the slurries of the invention that are curable thermally, or thermally and with actinic radiation, may comprise crosslinking agents which contain complementary reactive functional groups for thermal crosslinking and/or reactive functional groups containing at least one bond which can be activated with actinic radiation.

Suitable crosslinking agents are all crosslinking agents that are customary in the field of light-stable clearcoats. Examples of suitable crosslinking agents are

-   -   amino resins, as described for example in Römpp Lexikon Lacke         und Druckfarben, Georg Thieme Verlag, 1998, page 29, “amino         resins”, in the textbook “Lackadditive” [Additives for coatings]         by Johan Bieleman, Wiley-VCH, Weinheim, N.Y., 1998, pages 242         ff., in the book “Paints, Coatings and Solvents”, second,         completely revised edition, edited by D. Stoye and W. Freitag,         Wiley-VCH, Weinheim, N.Y., 1998, pages 80 ff., in the patents         U.S. Pat. No. 4,710,542 A1 or EP 0 245 700 A1, and in the         article by B. Singh and coworkers, “Carbamylmethylated         Melamines, Novel Crosslinkers for the Coatings Industry”, in         Advanced Organic Coatings Science and Technology Series, 1991,         volume 13, pages 193 to 207;     -   carboxyl-containing compounds or resins, as described for         example in the patent DE 196 52 813 A1 or 198 41 408 A1,         especially 1, 12-dodecanedioic acid,     -   resins or compounds containing epoxide groups, as described for         example in the patents EP 0 299 420 A1, DE 22 14 650 B1, DE 27         49 576 B1, U.S. Pat. Nos. 4,091,048 A or 3,781,379 A;     -   tris(alkoxycarbonylamino)triazines, as described in the patents         U.S. Pat. Nos. 4,939,213 A, 5,084,541 A, 5,288,865 A or in the         patent application EP 0 604 922 A;     -   blocked polyisocyanates, as described for example in the patents         U.S. Pat. No. 4,444,954 A1, DE 196 17 086 A1, DE 196 31 269 A1,         EP 0 004 571 A1 or EP 0 582 051 A1; or     -   beta-hydroxyalkylamides such as         N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide or         N,N,N′,N′-tetrakis(2-hydroxypropyl)adipamide.

The crosslinking agents described above may be used individually or as a mixture of at least two crosslinking agents. In accordance with the invention, the blocked polyisocyanates and/or tris(alkoxy-carbonylamino)triazines, especially the blocked poly-isocyanates, afford particular advantages and are therefore used with particular preference.

The amount of crosslinking agent(s) in the dimensionally stable particles of the slurry of the invention may likewise vary widely and is guided primarily by the functionality and amount of the binders on the one hand and by the functionality of the crosslinking agents on the other. The amount is preferably from 10 to 95%, more preferably from 12 to 94%, with particular preference from 14 to 93%, with very particular preference from 16 to 92%, and in particular from 18 to 90% by weight, based in each case on the solids of the slurry of the invention.

In addition to the essential constituents described above, the dimensionally stable particles of the slurry of the invention may comprise additives such as are commonly used in clearcoat materials. It is essential that these additives do not substantially lower the glass transition temperature, Tg, of the binders.

Examples of suitable additives are polymers (other than the above-described binders and crosslinking agents), crosslinking catalysts, defoamers, adhesion promoters, additives for improving substrate wetting, additives for improving surface smoothness, flatting agents, light stabilizers, corrosion inhibitors, biocides, flame retardants, and polymerization inhibitors, especially photoinhibitors, as described in the book “Lackadditive” by Johan Bieleman, Wiley-VCH, Weinheim, N.Y., 1998.

Moreover, the dimensionally stable particles may also comprise constituents curable with actinic radiation, different than the binders described above, as additives if the slurry of the invention is to be curable thermally and with actinic radiation or with actinic radiation alone. Examples of such constituents include

-   -   the binders envisaged for use in UV-curable clearcoat materials         and powder clearcoat materials and described in the European         patent applications EP 0 928 800 A1, EP 0 636 669 A1, EP 0 410         242 A1, EP 0 783 534 A1, EP 0 650 978 A1, EP 0 650 979 A1, EP 0         650 985 A1, EP 0 540 884 A1, EP 0 568 967 A1, EP 0 054 505 A1 or         EP 0 002 866 A1, the German patent applications DE 197 09 467         A1, DE 42 03 278 A1, DE 33 16 593 A1, DE 38 36 370 A1, DE 24 36         186 A1 or DE 20 03 579 B1, the international patent applications         WO 97/46549 or WO 99/14254 or the American patents U.S. Pat.         Nos. 5,824,373 A, 4,675,234 A, 4,634,602 A, 4,424,252 A,         4,208,313 A, 4,163,810 A, 4,129,488 A, 4,064,161 A or 3,974,303         A;     -   reactive diluents curable with actinic radiation, such as those         described in Römpp Lexikon Lacke und Druckfarben, Georg Thieme         Verlag, Stuttgart, N.Y., 1998, on page 491 under the headword         “reactive diluents”; or     -   photoinitiators as described in Römpp Chemie Lexikon, 9th,         expanded and revised edition, Georg Thieme Verlag, Stuttgart,         vol. 4, 1991, or in Römpp Lexikon Lacke und Druckfarben, Georg         Thieme Verlag, Stuttgart, 1998, pages 444 to 446.

The slurry of the invention may likewise comprise additives in the aqueous phase.

Preferably, the additives in question are nonionic and/or ionic thickeners. This effectively counters the tendency of the comparatively large solid particles toward sedimentation.

Examples of nonionic thickeners are hydroxyethyl-cellulose and polyvinyl alcohols. So-called nonionic associative thickeners are likewise available on the market in a diverse selection. They generally comprise water-dilutable polyurethanes which are reaction products of water-soluble polyetherdiols, aliphatic diisocyanates, and monofunctional hydroxyl compounds with an organophilic radical.

Likewise available commercially are ionic thickeners. These normally contain anionic groups and are based in particular on special polyacrylate resins with acid groups, some or all of which may have been neutralized.

Examples of suitable thickeners for use in accordance with the invention are known from the text book “Lackadditive” by Johan Bieleman, Wiley-VCH, Weinheim, N.Y., 1998, pages 31 to 65, or from the German patent application DE 199 08 018 A1, page 13, line 18 to page 14, line 48.

For the slurry of the invention it may be advantageous if both of the above-described types of thickener are present therein. In by far the majority of cases, however, one thickener is sufficient, particularly a nonionic thickener, to provide the desired pseudo-plasticity.

The amount of thickeners to be added, and, where two different thickeners are employed, the ratio of ionic to nonionic thickener, are guided by the desired viscosity of the slurry of the invention, which in turn is determined by the required sedimentation stability and the specific requirements of spray application. The skilled worker is therefore able to determine the amount of the thickeners and, where appropriate, the ratio of the thickener types to one another on the basis of simple considerations, possibly with the aid of preliminary tests.

The viscosity is preferably set to within a range from 50 to 1 500 mPas at a shear rate of 1 000 s⁻¹ and from 150 to 8 000 mPas at a shear rate of 10 s⁻¹, and also from 180 to 12 000 mPas at a shear rate of 1 s⁻¹.

This viscosity behavior, known as “pseudoplasticity”, describes a state which does justice both to the requirements of spray application, on the one hand, and to the requirements in terms of storage and sedimentation stability, on the other: in the state of motion, such as when pumping the slurry of the invention in circulation in the ring circuit of the coating plant and when spraying, for example, the slurry of the invention adopts a state of low viscosity which ensures easy processability. In the absence of shear stress, on the other hand, the viscosity rises and thus ensures that the coating material already present on the substrate to be coated has a reduced tendency to form runs on vertical surfaces. In the same way, a result of the higher viscosity in the stationary state, such as during storage, for instance, is that sedimentation of the solid particles is very largely prevented or that any slight degree of settling of the slurry of the invention during the storage period can be removed again by agitation.

The aqueous phase of the slurry of the invention may further comprise leveling assistants which can be incorporated in the film by crosslinking. Examples of suitable constituents of this kind are thermally curable reactive diluents such as positionally isomeric diethyloctanediols or hydroxyl-containing hyperbranched compounds or dendrimers such as are described in the German patent applications DE 198 05 421 A1, DE 198 09 643 A1 or DE 198 40 405 A1.

In its aqueous phase the slurry of the invention may further comprise at least one, especially one, water-soluble salt, preferably in an amount of from 0.1 to 50 mmol per 1 000 g of water in the slurry of the invention. The salt is decomposable without residue or substantially without residue. This means that its decomposition is not accompanied by the formation of any residues at all, or is accompanied only by the formation of residues in an amount which induces no deleterious technical effects in the clearcoats of the invention.

The salt may be decomposable by means of heat and/or actinic radiation. Preferably, it is thermally decomposable. It is preferably decomposable under the conditions of the curing of the clearcoat films of the invention produced from the slurries of the invention. It is of advantage in accordance with the invention if the salt is decomposable at temperatures above 100° C. The decomposition of the salt is preferably at an end at 250° C., more preferably 200° C., with particular preference 190° C., and in particular 180° C.

The decomposition of the salt may be accompanied by formation of any of a very wide variety of organic, inorganic and organometallic decomposition products. The decomposition products, accordingly, may comprise volatile elements, neutral organic or inorganic hydrogen compounds, organic and inorganic bases, organic and inorganic acids, or oxides.

Examples of volatile elements are phosphorus, sulfur, nitrogen and oxygen, especially nitrogen.

Examples of neutral organic and inorganic hydrogen compounds are water and hydrocarbons, especially water.

Examples of organic and inorganic bases are ammonia, methylamine, dimethylamine and trimethylamine, especially ammonia.

Examples of organic and inorganic acids are formic acid, acetic acid, propionic acid, oxalic acid, citric acid, tartaric acid, hydrochloric acid, hydrogen bromide, phosphoric acid, phosphorous acid, amidosulfonic acid, sulfuric acid, sulfurous acid, thiosulfuric acid, HSCN and hydrogen sulfide, especially acetic acid.

Examples of oxides are carbon dioxide, sulfur dioxide, sulfur trioxide and phosphorus oxide, especially carbon dioxide.

It is preferred to select a salt whose decomposition products are of little or no toxicity and/or of little or no corrosiveness. Preference is given to selecting a salt which forms, as its decomposition products, water, nitrogen, carbon dioxide, ammonia and organic acids.

With particular preference, the salt is selected from the group of ammonium salts, with very particular preference from the group consisting of salts of ammonia and of organic amines with organic and inorganic acids.

The ammonium salt is selected in particular from the group consisting of ammonium carbonate, ammonium thiocyanate, ammonium sulfamate, ammonium sulfite monohydrate, ammonium formate, ammonium acetate, ammonium hydrogen oxalate monohydrate, diammonium oxalate monohydrate, ammonium citrate, and ammonium tartrate. Of these, in turn, ammonium carbonate and ammonium acetate are very particularly advantageous and are therefore used with very particular preference in accordance with the invention.

The slurry of the invention is preferably prepared by the secondary dispersion processes from the German patent application DE 199 08 018 A1 or from the German patent DE 198 41 842 C2 or described in the German patent application 100 55 464.4, unpublished at the priority date of the present specification.

For this process, the ionically stabilizable binders and the crosslinking agents and also, where appropriate, the additives are mixed in organic solution and dispersed together in water with the aid of neutralizing agents. The dispersion is then diluted with water, while stirring. To start with a water-in-oil emulsion is formed, which on further dilution is transformed into an oil-in-water emulsion. This point is generally reached at solids contents of <50% by weight, based on the emulsion, and is evident externally from a relatively sharp fall in viscosity in the course of the dilution.

The oil-in-water emulsion may also be prepared directly by the melt emulsification of the binders and of the crosslinking agents and also, where appropriate, of the additives in water.

It is of advantage in accordance with the invention if the wetting agents for use in accordance with the invention are added to the organic solution and/or to the water before or during emulsification. They are preferably added to the organic solution.

The resulting emulsion, which still contains solvents, is subsequently freed from its solvents by azeotropic distillation.

In accordance with the invention it is of advantage if the solvents to be removed are distilled off at a distillation temperature below 70° C., preferably below 50° C., and in particular below 40° C. If desired, the distillation pressure is chosen so that this temperature range is observed in the case of relatively higher-boiling solvents.

At its most simple, the azeotropic distillation may be effected by stirring the emulsion at room temperature in an open vessel for several days. Preferably, the solvent-containing emulsion is freed from its solvents by vacuum distillation.

In order to avoid high viscosities, the amount of water and solvents removed by evaporation or distillation is replaced by water. The water may be added before, during, or after the evaporation or distillation, by addition in portions.

Following the loss of solvents, the glass transition temperature, Tg, of the dispersed particles rises and a dispersion, i.e. the slurry of the invention, forms instead of the previous solvent-containing emulsion.

The salts for use in accordance with the invention may be introduced into the slurries of the invention, or their precursors, in a variety of ways. For example, the salts may be added to customary and known clearcoat slurries to give the slurries of the invention. They may also be added to the organic solution of constituents of the powder slurry of the invention. Preferably, they are dissolved in the water prior to the emulsification of the organic solution.

If desired, the particles of the slurry of the invention are mechanically comminuted in the wet state, a procedure also referred to as wet grinding. In the course of this treatment it is preferred to employ conditions such that the temperature of the material being ground does not exceed 70° C., more preferably 60° C., and in particular 50° C. The specific energy input during the grinding process is preferably from 10 to 1 000, more preferably from 15 to 750, and in particular from 20 to 500 Wh/g.

For wet grinding it is possible to employ a very wide variety of equipment which produces high or low shear fields.

Examples of suitable equipment producing low shear fields are customary and known stirred tanks, slot homogenizers, microfluidizers, and dissolvers.

Examples of suitable equipment producing high shear fields are customary and known stirred mills and inline dissolvers.

Particular preference is given to employing the equipment which produces high shear fields. Of this equipment, the stirred mills are particularly advantageous in accordance with the invention and are therefore used with very particular preference.

During wet grinding, generally, the slurry of the invention is supplied to the above-described equipment, and circulated therein, by means of appropriate devices, such as pumps, in particular gear pumps, until the desired particle size has been reached.

The slurry of the invention advantageously has a solids content of from 10 to 60% by weight, in particular from 20 to 50% by weight.

The slurry of the invention is preferably filtered prior to its use. This is done using the customary and known filtration equipment and filters, such as are also suitable for filtering the known clearcoat slurries. The mesh size of the filters may vary widely and is guided primarily by the size and size distribution of the particles of the slurry of the invention. The skilled worker is therefore easily able to determine the appropriate filters on the basis of this physical parameter. Examples of suitable filters are monofilament flat filters or bag filters. These are available on the market under the brand names Pong® or Cuno®. It is preferred to use bag filters having mesh sizes of from 25 to 50 μm, examples being Pong® 25 to Pong® 50.

To produce the clearcoats of the invention, the slurry of the invention is applied to the substrate that is to be coated. No special measures need be taken here; instead, the application may take place in accordance with the customary and known processes, which is another particular advantage of the slurry of the invention.

Following its application, the slurry of the invention dries without problems and does not film at the processing temperature, generally at room temperature. In other words, the slurry of the invention, applied as a wet film, loses water when flashed off at room temperature or slightly elevated temperatures, with the particles present therein changing their original form. As a result, the tendency toward mudcracking is extremely low.

In the subsequent baking step, the now substantially water-free powder layer is caused to crosslink. In some cases it may be of advantage to carry out the leveling process and the crosslinking reaction with a chronological offset, by operating a staged heating program or a so-called heating ramp. The crosslinking temperature that is appropriate for the present examples is situated between 120 and 160° C. The corresponding baking time is between 20 and 60 minutes.

In the case of the dual-cure slurry of the invention, thermal curing is supplemented by curing with actinic radiation, which may be carried out using the customary and known radiation sources and processes, such as are described, for example, in the German patent application DE 198 18 735 A1, column 10, line 31 to column 11, line 22. These processes and equipment may also be used to cure the slurry of the invention that is curable with actinic radiation.

The resultant clearcoat has outstanding performance properties. For instance, it adheres firmly to all customary and known basecoats or to substrates such as metal, glass, wood, ceramic, stone, concrete or plastic. It is of high gloss, smooth, scratch-resistant, stable to weathering and chemicals, and even at high coat thicknesses is free from defects, such as stress cracks or popping marks. It no longer exhibits any blushing on exposure to moisture. Furthermore, it is free from microdefects and displays no disruptive optical effects, such as a starry sky that is similar to the metallic effect.

Above all, however, the slurry of the invention possesses very good filterability in combination with very good gear pump conveyability.

On the basis of this advantageous profile of properties, the slurry of the invention is outstandingly suitable for automotive OEM finishing, automotive refinish, the interior and exterior painting of buildings, the coating of doors, windows and furniture, and industrial coating, including coil coating, container coating, the coating of small parts, the impregnation and/or coating of electrical components, or the coating of white goods. It is used in particular to produce clearcoats as part of multicoat color and/or effect paint systems, which are produced from basecoat materials and the slurry of the invention by the customary and known wet-on-wet techniques.

For the wet-on-wet technique, the slurry of the invention may readily be combined with numerous basecoat materials, especially aqueous basecoat materials, without the occurrence of problems, such as cracking, lack of wettability, or poor intercoat adhesion.

The slurry of the invention may surprisingly also be used as an adhesive for producing adhesive films and as a sealing compound for producing seals, especially in the technical fields referred to above.

INVENTIVE AND COMPARATIVE EXAMPLES Preparation Example 1

The preparation of a methacrylate copolymer (binder) for inventive use

39.75 parts by weight of methyl ethyl ketone were charged to a reaction vessel equipped with stirrer, reflux condenser, oil heating, nitrogen inlet pipe and two feed vessels, and this initial charge was heated to 78° C.

Thereafter, an initiator solution of 4 parts by weight of methyl ethyl ketone and 5 parts by weight of TBPEH was metered in at a uniform rate from the first feed vessel over the course of 6.75 h.

Fifteen minutes after the beginning of the initiator feed, a monomer mixture of 27.5 parts by weight of n-butyl methacrylate, 9.15 parts by weight of i-butyl methacrylate, 12.75 parts by weight of hydroxyethyl methacrylate and 0.6 part by weight of methacrylic acid was metered in at a uniform rate from the second feed vessel over the course of 6 h. The monomer line was then flushed with 0.25 part by weight of methyl ethyl ketone and the feed vessel with 0.5 part by weight of methyl ethyl ketone. After the end of the initiator feed, the feed vessel in question was likewise flushed with 0.5 part by weight of methyl ethyl ketone.

The reaction mixture was left to react at 78° C. for a further 3 h. The volatile fractions were then removed by vacuum distillation until the solids content was 70% by weight. The resin solution was then discharged. It had a viscosity of from 7.0 to 10.0 dPas (resin solids, 60 percent, xylene, at 23° C.). The acid number was from 9.0 to 11.0 and the hydroxyl number was 110 mg KOH/g resin solids.

Preparation Example 2

The preparation of a blocked polyisocyanate based on hexamethylene diisocyanate

534 parts by weight of Desmodur® N 3300 (commercial isocyanurate of hexamethylene diisocyanate from Bayer AG) and 200 parts by weight of methyl ethyl ketone were charged to a reaction vessel and this initial charge was heated to 40° C. 100 parts by weight of 2,5-dimethylpyrazole were added to the solution, with cooling, and the subsidence of the exothermic reaction was awaited. Thereafter, with continued cooling, a further 100 parts by weight of 2,5-dimethylpyrazole were added. After the exothermic reaction had again subsided, a further 66 parts by weight of 2,5-dimethyl-pyrazole were added. Cooling was then switched off, as a result of which the reaction mixture slowly warmed up to 80° C. It was held at this temperature until its isocyanate content had fallen to below 0.1%. The reaction mixture was then cooled and discharged.

The resulting solution of the blocked polyisocyanate had a solids content of 81% by weight (1 h at 130° C.) and a viscosity of 3.4 dPas (70% in methyl ethyl ketone; cone and plate viscometer at 23° C.).

Inventive Examples 1 to 4 and Comparative Examples C1 and C2

The preparation of inventive slurries (examples 1 to 4) and noninventive slurries (examples C1 and C2), and their performance properties

Example 1

961.8 parts by weight of the methacrylate copolymer solution from preparation example 1 and 484.6 parts by weight of the solution of the blocked polyisocyanate from preparation example 2 were mixed with one another at room temperature in an open stirred vessel for 15 minutes. The resulting mixture was admixed with 21.5 parts by weight of Tinuvin® 400 and 10.7 parts by weight of Tinuvin® 123 (commercial light stabilizers from Ciba Specialty Chemicals, Inc.) and 15 parts by weight of Lutensol® AT 50 (ethoxylated alcohol having from 16 to 18 carbon atoms in the alkyl radical and containing on average per molecule 50 ethylene oxide groups, from BASF Aktiengesellschaft), after which the mixture was stirred at room temperature for 30 minutes. Then 0.86 part by weight of dibutyltin dilaurate and 4.68 parts by weight of dimethylethanolamine were added. The resulting mixture was stirred at room temperature for a further two hours.

Subsequently, 735 parts by weight of deionized water in which 1.462 parts by weight of ammonium acetate had been dissolved were added in small portions to the mixture. After an interval of 15 minutes, a further 780 parts by weight of deionized water were added at a uniform rate over the course of 30 minutes.

The resulting aqueous emulsion was diluted with 739 parts by weight of deionized water. After that the same amount of a mixture of volatile organic solvents and water was removed from it under reduced pressure on a rotary evaporator, until the solids content was 37% by weight (1 h at 130° C.).

To set the desired pseudoplasticity, 90 parts by weight of Acrysol® RM-8W (commercial nonionic associative thickener from Rohm & Haas) and 1.57 parts by weight of Baysilon® AI 3468 (commercial leveling agent from Bayer AG) were stirred into the slurry.

Example 2

Example 1 was repeated except that the Lutensol® AT 50 was added to the aqueous phase prior to emulsification.

Example 3

Example 1 was repeated except that, instead of Lutensol® AT 50, Lutensol® AT 25 (ethoxylated fatty alcohol having from 16 to 18 carbon atoms in the alkyl radical and containing on average per molecule 25 ethylene oxide groups, from BASF Aktiengesellschaft) was used.

Example 4

Example 2 was repeated but using Lutensol® AT 25 instead of Lutensol® AT 50.

Example C1

Example 3 was repeated except that Lutensol® AT 25 was added to the finished clearcoat slurry.

Example C2

Example C1 was repeated but using no wetting agent.

Table 1 gives an overview of the particle sizes, pseudoplasticity properties, and filterability of the slurries, before and after passage five times through a gear pump.

The results compiled in table 1 underscore the fact that only the inventive slurries had very good filterability and very good gear pump conveyability. The attenuation in pseudoplasticity brought about by the wetting agents for use in accordance with the invention was acceptable. Moreover, the test results show that the wetting agents are most effective if they are added prior to the emulsification in the course of the secondary dispersion process.

TABLE 1 Particle sizes, pseudoplasticity and filterability of the slurries of the invention (examples 1 to 4) and of the noninventive slurries (examples C1 and C2) Examples: Properties 1 2 3 4 C1 C2 Particle size (μm)^(a)) prior to addition of thickener: average particle size 6.13 7.16 3.69 2.84 4.26 6.81 d90 (90% of the particles <) 10.28 13.36 7.76 4.81 9.19 15.12 Following addition of thickener: average particle size 6.07 6.89 3.73 2.66 4.32 6.78 d90 (90% of the particles <) 10.32 12.22 8.17 5.29 9.7 15.2 Viscosity^(b)) (dPas) Shear rate (s⁻¹): 10 87 209 224 434 751 904 100 45 129 137 244 469 129 1 000 29 79 73 131 229 66 Filterability^(c)): Amount (g) passing through at mesh size: 25 μm 1 943 2 500 2 360 2 410 445 0 50 μm — — — — — 336 Filterability^(d)): Amount (g) passing through at mesh size: 25 μm 1 880 1 200 2 191 450 0 0 50 μm — — — — — — Filterability^(e)): After 5-fold passage through the gear pump: Amount (g) passing through at mesh size 25 μm 107 67 93 300 0 0 ^(a))Laser diffraction method (instrument from Malvern); ^(b))Cone and plate viscometer at 18° C.; ^(c))Bag filter platelet, amount of slurry used: 2 500 g; ^(d))Bag filter platelet, amount of slurry used: 2 500 g, standing time of the slurries: 4 days; ^(e))Bag filter platelet, amount of slurry used: 2 500 g.

In a first series, the unstressed filtered inventive slurries of examples 1 to 4 and the unstressed filtered noninventive slurry of example C2 were applied in wedge form to metal test panels and baked at 145° C. for 30 minutes.

In a second series, the stressed filtered inventive slurries of examples 1 to 4 and the stressed filtered noninventive slurry of example C2 were applied in wedge form to metal test panels and again baked at 145° C. for 30 minutes.

The clearcoats of examples 1 to 4 and of example C2, applied in wedge form, were used to determine the film thicknesses starting from which edge popping marks and flat-area popping marks occurred. Also determined were the film thicknesses starting from which wetting of the substrate (cathodic electrocoat, CE, and “black as night” basecoat, BC) occurred. The results can be found in table 2.

TABLE 2 Flow properties and wetting behavior of the inventive clearcoats 1 to 4 and of the noninventive clearcoat C2 Examples: Properties 1 2 3 4 C2 Unstressed slurry: From film thickness (μm) Edge popping: 168 145 150 150 160 Flat-area popping: 89 79 90 89 76 From film thickness (μm) Wetting of CE: 24 18 15 15 19 BC: 28 11 11 19 19 Stressed slurry: From film thickness (μm) Edge popping: 166 150 163 149 not measured Flat-area popping: 73 86 61 80 not measured From film thickness (μm) Wetting of CE: 25 18 18 15 not measured BC: 12 15 14 11 not measured EC: Cathodic electrocoat; BC: “black as night” basecoat.

For a third series, a so-called integrated system was prepared using a black basecoat material.

For this purpose, steel panels coated cathodically with commercially customary electrocoat material were first of all coated with a functional coat (Ecoprime®; BASF Coatings AG) using a gravity-feed cup gun. After a 5-minute flashoff at room temperature, a black aqueous basecoat material (Ecostar®; BASF Coatings AG) was applied to the functional coat in the same way and then dried initially at 80° C. for 5 minutes.

After the panels have cooled, the stressed filtered inventive slurries of examples 1 to 4 were applied in the same way. The panels were then flashed off for 5 minutes and then dried initially at 40° C. for 15 minutes. Thereafter, they were baked in a horizontal position at 145° C. for 30 minutes.

The applied wet films were chosen so that, after baking, the dry film thicknesses for the functional coat and for the aqueous basecoat were each 15 μm.

Important performance properties of the inventive clearcoats 1 to 4 can be found in table 3.

TABLE 3 Flow properties (wave scan) and gloss/haze of the inventive clearcoats 1 to 4 Examples Properties 1 2 3 4 Film thickness (μm) 54 46 52 45 Gloss/haze (20°) to  83/11  83/12  83/5  83/5 DIN 67530: Wave scan^(a))   3.2/14.1   2.6/14.5   2.7/13.6   3.3/12.9 Longwave/shortwave ^(a))Instrument: Byk/Gardner - wave scan plus.

The gloss and the flow were very good. The chemical resistance of the inventive clearcoats was likewise very good. 

1. A pseudoplastic clearcoat slurry, comprising: particles that are dimensionally stable under storage and application conditions; and at least one wetting agent comprising at least one alkoxylated fatty alcohol having from 16 to 18 carbon atoms in the alkyl radical and comprising on average per molecule at least 25 oxaalkanediyl groups; wherein the particles have an average size of from 3 to 20 μm and a maximum size of 30 μm; wherein the viscosity of the pseudoplastic clearcoat slurry increases with decreasing shear; and wherein the pseudoplastic clearcoat slurry is curable thermally or thermally and with actinic radiation.
 2. The pseudoplastic clearcoat slurry of claim 1, wherein the wetting agent comprises on average per molecule at least 45 oxaalkanediyl groups.
 3. The pseudoplastic clearcoat slurry of claim 1, wherein the oxaalkanediyl groups are selected from the group consisting of 1-oxapropane-1,3-diyl, 1-oxabutane-1,4-diyl, 1-oxabutane-1,3-diyl, 1-oxapentane-1,5-diyl, 1-oxapentane-1,3-diyl, and combinations thereof.
 4. The pseudoplastic clearcoat slurry of claim 1, wherein the oxaalkanediyl groups are selected from the group consisting of 1-oxapropane-1,3-diyl, 1-oxabutane-1,3-diyl, and combinations thereof.
 5. The pseudoplastic clearcoat slurry of claim 1, wherein the oxaalkanediyl group is 1-oxapropane-1,3-diyl.
 6. The pseudoplastic clearcoat slurry of claim 1, wherein the at least one wetting agent is present in an amount of from 0.01 to 2.5% by weight of the clearcoat slurry.
 7. The pseudoplastic clearcoat slurry of claim 1, further comprising at least one water-soluble salt, optionally wherein the salt can be decomposed without residue.
 8. The pseudoplastic clearcoat slurry of claim 7, wherein the at least one water-soluble salt is decomposable under the conditions of curing of the clearcoat slurry.
 9. The pseudoplastic clearcoat slurry of claim 7, wherein the at least one water-soluble salt is decomposable thermally and/or with actinic radiation.
 10. The pseudoplastic clearcoat slurry of claim 7, wherein the at least one water-soluble salt is thermally decomposable.
 11. The pseudoplastic clearcoat slurry of claim 7, wherein the at least one water-soluble salt is an ammonium salt.
 12. The pseudoplastic clearcoat slurry of claim 11, wherein the at least one water-soluble salt is selected from the group consisting of ammonium carbonate, ammonium thiocyanate, ammonium sulfamate, ammonium sulfite monohydrate, ammonium formate, ammonium acetate, ammonium hydrogen oxalate monohydrate, diammonium oxalate monohydrate, ammonium citrate, and combinations thereof.
 13. The pseudoplastic clearcoat slurry of claim 11, wherein the at least one water-soluble salt is selected from the group consisting of ammonium carbonate, ammonium acetate, and combinations thereof.
 14. The pseudoplastic clearcoat slurry of claim 1, wherein the dimensionally stable particles comprise binders comprising at least one methacrylate copolymer comprising in copolymerized form, based on the at least one methacrylate copolymer, at least 90% by weight of at least one methacrylate comonomer, and wherein at least one monomer for the copolymer comprises at least one (meth)acrylate comonomer comprising potentially ionic groups.
 15. The pseudoplastic clearcoat slurry of claim 14, wherein the at least one methacrylate copolymer comprises in copolymerized form, based on the at least one methacrylate copolymer, more than 99% by weight of at least one methacrylate comonomer, and wherein at least one monomer for the copolymer comprises at least one (meth)acrylate comonomer comprising potentially ionic groups.
 16. The pseudoplastic clearcoat slurry of claim 14, wherein the at least one (meth)acrylate comonomer comprising potentially ionic groups is selected from the group consisting of acrylic acid, beta-carboxyethyl acrylate, methacrylic acid, and combinations thereof.
 17. The pseudoplastic clearcoat slurry of claim 1, wherein the slurry has an organic solvent content of less than 3% by weight.
 18. The pseudoplastic clearcoat slurry of claim 1, prepared by a process comprising: 1) emulsifying the dimensionally stable particles in an organic solvent solution in water to give an emulsion of the oil-in-water type, 2) removing the organic solvent, and 3) replacing at least some of a volume of the organic solvent removed with water, wherein the at least one wetting agent is added to the organic solvent solution, the water, or a combination thereof, prior to step 1) of the process.
 19. A method comprising applying the clearcoat slurry of claim 1 to a substrate as one of an automotive OEM finish, an automotive refinish, a building paint, a door coating, a window coating, a furniture coating, an industrial coating, a coil coating, a container coating, an electrical component impregnation, an electrical component coating, a white goods coating, an adhesive, or a sealing compound.
 20. The method of claim 19, wherein the clearcoat slurry is applied to a substrate to produce at least one clearcoat as a part of a multicoat color and/or effect paint system.
 21. The pseudoplastic clearcoat slurry of claim 1, wherein the slurry has a viscosity from 50 to 1500 mPas at a shear rate of 1000 s⁻¹, from 150 to 8000 mPas at a shear rate of 10 s⁻¹, and from 180 to 12000 mPas at a shear rate of 1 s⁻¹. 